An Overview of Knife Blade Steel and Its Importance in Knife Performance
Posted by carbonsteel on December 24th, 2020
Blade material is an extremely important aspect of any knife. And there are many types of steel used for knife blades. Some are relatively soft steels, which may dull fairly quickly but be easily re-sharpened. Other steels may be very hard, and so can be ground to an extremely sharp edge, but they may be susceptible to chipping or break easily if used inappropriately (for prying, for example).
In the world of knife steel, there is always a compromise between strength (ductility, or the ability to bend rather than snap), hardness (ability to withstand impact without deforming), edge-retention, and corrosion-resistance. Typically, as one characteristic increases, another will decrease.
For example, some of the strongest, toughest knives are only moderately sharp (comparatively speaking), and are very susceptible to rust. But with proper maintenance, they can offer a lifetime of hard use that would damage or destroy a knife made from a different kind of steel.
The choice of blade steel will impact the appropriate usage of the knife, its ease or difficulty of manufacture, and of course, its price. Let's have a brief look at some of the more popular choices of blade steel available.
A Brief Primer on Blade Steel
All steel is composed of iron, with some carbon added to it. Various grades and types of steels are created by adding other "alloying" elements to the mixture. "Stainless" steel, by definition, contains at least 13% chromium. "Non-Stainless" steels are also known as carbon steels or alloy steels.
Despite its name and late-night TV reputation, stainless steel is not stainless. Like all steel, it too will rust. The high chromium level in stainless helps to decrease corrosion, but cannot entirely prevent it. Only proper maintenance and handling will keep your knife completely rust free. (And basically, that simply means keeping it clean and dry, lightly oiling it from time to time, and not storing it in a sheath. Just that simple. Oh yeah: no dishwashers. Ever.)
Speaking very generally, there are three grades of steel used for knife blades: Good, Better and Best. Each type of steel has unique properties that make it more suitable to specific designs and applications. And of course, the choice of steel will impact the knife's price. In the event you loved this post and you would love to receive more details with regards to 8cr13mov steel composition visit the website.
Good Blade Steel
Knives utilizing "Good" steel blades should be considered entry-level, and tend to be made from rust-resistant (not rust-free -- see above) stainless steel. Typically manufactured in Asia, these knives offer a fairly good economic value. These blades are usually 'softer' and therefore require more frequent sharpening to keep the edge performing well. But, because they are in fact 'softer,' re-sharpening is fairly easy. Some of the more popular stainless steel blade materials in this class are 420, 440A and 7Cr13MoV.
420 stainless steel has a little less carbon than 440A. Many knife makers use 420 because it's inexpensive and it resists corrosion fairly well. 420 steel sharpens easily and is found in both knives and tools.
The relative low-cost and high corrosion resistance of 440A stainless steel makes it ideal for kitchen-grade cutlery. While exhibiting similar characteristics to the better-grade AUS 6 steel, it is considerably less expensive to produce. 440A contains more carbon than 420, and is therefore a 'harder' steel. This allows better edge retention than a blade made from 420, but is more difficult to re-sharpen.
7Cr13MoV is a good blade steel, that has the alloying elements molybdenum (Mo) and vanadium (V) added to the matrix. Molybdenum adds strength, hardness and toughness to the steel, while also improving its machinability. Vanadium adds strength, wear-resistance and toughness. Vanadium also provides corrosion resistance, which is seen in the oxide coating on the blade.
Better Blade Steel
Better grade stainless steel blades contain a higher chromium (Cr) content than their entry-level counterparts. Since the amount of chromium is increased in the manufacturing process, these blades are more expensive. Chromium provides a greater edge holding capability, which means that the blade will require less frequent sharpening. These better grade knives sharpen reasonably easily, but it's important to employ proper sharpening techniques. The combination of great value and performance make these blades perfect for everyday use. Examples of these types of steel are AUS 6, AUS 8, 440C and 8Cr13MoV.
Both AUS 6 and AUS 8 are high-grade chromium Japanese steels, which provide a great balance of toughness, strength, edge retention and corrosion resistance, all at a moderate cost. These blade steels will measure a hardness of 56-58 on the Rockwell hardness scale (HRc). The carbon content of AUS 8 is close to 0.75%, which makes it very suitable as a blade steel. AUS 6 and AUS 8 are very popular with many knife manufacturers because they are both cost-effective and good-performing steels.
440C is a reasonably high-grade cutlery steel, similar to the AUS series. However, 440C contains more carbon, which increases the steel's hardness. Its toughness and relative low-cost make 440C stainless steel appealing to many knife manufacturers for their mid-range knife series.
The Chinese stainless steel 8Cr13MoV has a high performance-to-cost ratio. It is often compared to AUS 8. 8Cr13MoV is tempered to a hardness range of 56-58 on the Rockwell scale. This relatively high hardness can be attributed to the steel's higher molybdenum and vanadium content.