Tempered glass processing methods plus characteristicsPosted by Snow Lysgaard on January 22nd, 2021 insualted glass fabricator processing methods Tempered glass (also often known as tempered glass) is a good general term for reinforced goblet products with great technical properties and high temperature gerüttel properties. Tempered wine glass will be divided into level tempered cup and bent tempered cup for cup doors together with microsoft windows, rupture walls together with glass bathroom walls associated with structures, since well as entrance doors plus windows for automobiles plus ships. Let's take a good look at typically the control methods of tempered wine glass and the characteristics regarding reinforced glass. The tempered glass processing method generally switches into physical tempering method, that is, the flat wine glass is put in a home heating central heat, warm to around its softening temperature (about 650 ° C) and kept for the certain time period (generally three to five rain), in addition to then removed from the heating central heat and well then utilized to nozzle The ice cold air is sprayed about both equally sides of this glass to make it quickly in addition to evenly chilled. After cooling to area heat range, it becomes a high-strength tempered glass. Once the tempered glass is damaged, the strain collapses and breaks in to numerous small pieces without having sharp edges and edges, which is not easy to hurt, so it is named safety glass. Reinforced goblet according to the state of fracture (the highest body weight of debris if cracked under certain circumstances will not exceed a good selected cost; the number regarding fragments in a specific area must surpass some sort of certain value) can be split up into three categories: My partner and i, II, III, and their very own marks will be TI, TII, TIII. Tempered glass features (1) Superior mechanical strength. The mechanical strength of tempered wine glass is 3-5 times over that regarding ordinary flat wine glass, together with it has the flexural energy can be not really less than 200 MPa. The impact weight is good. It is lowered from a level connected with 1. 2 m together with 0. 8 kg metallic balls, and the tempered mirror can remain complete with out broken.
(2) Great strength. A piece associated with 1200 ram × 350 ram × six milimeter tempered glass can produce a twisting deflection of a hundred (mm).
(3) High winter stability. Tempered glass is much less susceptible to bursting when encountered with quenching and rapid warmth. The maximum safe functioning heat is 288 ° Chemical, which can hold up against the heat range difference associated with 204 ° C.
Like it? Share it! |